汽轮机高压主汽门螺栓断裂失效分析

华电技术 ›› 2011, Vol. 33 ›› Issue (7): 26-27.

汽轮机高压主汽门螺栓断裂失效分析

董宇

天津军粮城发电有限公司，天津300300

收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2011-07-25

Analysis on fracture failure of bolt in highpressure main stop valve of steam turbine

DONG Yu

Tianjin Junliangcheng Power Generation Corporation Limited, Tianjin 300300, China

Received:1900-01-01 Revised:1900-01-01 Published:2011-07-25

摘要/Abstract

摘要： 某电厂汽轮机高压主汽门螺栓发生断裂失效，对材质为20Cr1Mo1VNbTiB的断裂螺栓进行了理化试验和失效分析。结果表明：主汽门螺栓在加工制造过程中热处理工艺控制不当，导致金相组织存在粗晶，机组运行过程中，螺栓高应力的粗晶区发生沿晶开裂并不断扩展，最终发生主汽门泄漏和螺栓断裂失效。给出了防止由于粗晶问题造成螺栓失效的措施。

关键词: 高压主汽门, 20Cr1Mo1VNbTiB, 宏观金相, 粗晶, 断裂

Abstract: The bolt of highpressure main stop valve of a power plant steam turbine was fractured. The physical and chemical test and the failure analysis for the fractured bolt, the material of which is 20Cr1Mo1VNbTiB, were carried out. The results show that during manufacturing process of the bolt of the main stop valve, the control of the heating processing was improper, and there was coarse grain in metallographic structure; in unit operation process, the intergranular crack occurred in coarse grain zone with high stress of the bolt, and the crack continuously extended. Finally, the leakage of the main stop valve and the bolt fracture failure were occurred. The measures to prevent the bolt failure caused by coarse grain were given.

Key words: high-pressure main stop valve, 20Cr1Mo1VNbTiB, macroscopic metallographic phase, coarse grain, fracture

董宇. 汽轮机高压主汽门螺栓断裂失效分析[J]. 华电技术, 2011, 33(7): 26-27.

DONG Yu. Analysis on fracture failure of bolt in highpressure main stop valve of steam turbine[J]. Huadian Technology, 2011, 33(7): 26-27.

[1]	吴红辉1,王韦2. 20Cr1Mo1VNbTiB高温螺栓断裂失效分析[J]. 华电技术, 2018, 40(10): 27-29.
[2]	桑长勇，杜福明，高全海，李新建. BBD3854磨煤机螺旋输送器故障原因分析与对策[J]. 华电技术, 2017, 39(3): 57-59.
[3]	王曦. 17CrNiMo6磨煤机减速机齿轮轴断裂原因分析[J]. 华电技术, 2017, 39(10): 58-59.
[4]	雷清华1，王建文2，王政2. 风电塔筒P&H基础预应力高强锚杆断裂分析[J]. 华电技术, 2016, 38(8): 34-36.
[5]	贺杰. 燃料加热器天然气管道断裂故障分析及处理[J]. 华电技术, 2016, 38(6): 38-40.
[6]	彭钦春，赵显国. 汽轮发电机顶轴油分配器螺栓断裂故障分析及处理[J]. 华电技术, 2016, 38(6): 55-56.
[7]	李艳军，牛保献. 电厂排粉机电机大轴断裂原因分析[J]. 华电技术, 2016, 38(11): 38-39.
[8]	徐敬民. 汽轮机高压主汽门阀杆断裂原因分析及修复[J]. 华电技术, 2015, 37(5): 44-45.
[9]	陈家权，刘福营，苏光耀，黄海鑫，吴根深. 超高压线夹端子断裂失效分析[J]. 华电技术, 2015, 37(4): 28-31.
[10]	贾少威. 空气压缩机轴颈断裂原因分析[J]. 华电技术, 2015, 37(11): 37-40.
[11]	杨小刚. 静叶可调轴流式引风机叶片磨损和断裂案例分析[J]. 华电技术, 2015, 37(10): 45-46.
[12]	冯玉锋. 斗轮堆取料机大轴断裂失效的原因分析[J]. 华电技术, 2014, 36(9): 37-39.
[13]	牛文献1，牛保献2. 某电厂循环水泵大轴断裂的原因分析[J]. 华电技术, 2014, 36(8): 27-29.
[14]	周凯. 直接空冷机组空冷岛轴流风机叶片断裂分析[J]. 华电技术, 2014, 36(2): 65-68.
[15]	侯健. 精密点检对高压电机转子笼条断裂的诊断应用分析[J]. 华电技术, 2013, 35(8): 52-53.