超临界锅炉试运行期间屏式过热器爆管原因分析

华电技术 ›› 2012, Vol. 34 ›› Issue (7): 34-37.

超临界锅炉试运行期间屏式过热器爆管原因分析

王甲安1，何桂宽1，乔立捷1，郭延军1，宋忠孝2

1.华电电力科学研究院，浙江杭州310030；2.西安交通大学，陕西西安71004

收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2012-07-25 发布日期:2012-07-25

Analysis on reason of tube cracking of platen superheater during commissioning of supercritical boiler

WANG Jiaan1, HE Guikuan1, QIAO Lijie1, GUO Yanjun1, SONG Zhongxiao2

1.China Huadian Electric Research Institute, Hangzhou 310030, China; 2.Xian Jiaotong University, Xian 710049, China

Received:1900-01-01 Revised:1900-01-01 Online:2012-07-25 Published:2012-07-25

摘要/Abstract

摘要： 某电厂超临界W火焰锅炉屏式过热器在试运行期间多次发生爆管事故，对原始管样、爆管管样及氧化皮状异物进行宏观检查、化学成分分析、拉伸性能试验、金相分析、扫描电镜及能谱分析等，结合停炉后内窥镜检查结果，查明爆管的主要原因是大量的原生态或次生态氧化皮状异物脱落堵塞屏式过热器入口集箱节流孔或管子，导致管子介质流量减小，使蒸汽对管子的冷却作用降低，局部处于超温状态，高温蠕变强度降低。

关键词: 超临界锅炉, 过热器管, 试运行, 氧化皮状物, 爆管

Abstract: In commissioning process of the platen superheater of supercritical Wshape flame boiler in a power plant, the tube cracking accident occurred repeatedly. The original tube sample, the cracked tube sample and substances similar to oxide skin were inspected by several methods, which include the macroscopic inspection, the chemical composition analysis, the tensile test, the metallographic analysis, the scanning electron microscope and the energy spectrum analysis. Combining with inspection result obtained by endoscope after the boiler shutdown, it was found that the main reason of pipe cracking is that a mass of original or subsequent oxide skin fell off and blocked the throttle orifices and pipe of the header in inlet of the platen superheater, which causes that the medium flow in the pipe reduced, the cooling effect of steam for the pipe became lower; and the local parts of pipe was over temperature, and its hightemperature creep strength decreased.

Key words: supercritical boiler, tube of superheater, commissioning, substances similar to oxide skin, tube cracking

王甲安;何桂宽;乔立捷;郭延军;宋忠孝. 超临界锅炉试运行期间屏式过热器爆管原因分析[J]. 华电技术, 2012, 34(7): 34-37.

WANG Jiaan;HE Guikuan;QIAO Lijie;GUO Yanjun;SONG Zhongxiao. Analysis on reason of tube cracking of platen superheater during commissioning of supercritical boiler[J]. Huadian Technology, 2012, 34(7): 34-37.

[1]	丛星亮, 谢红, 苏阳, 张骏, 程英捷. 660 MW超超临界二次再热机组深度调峰试验研究[J]. 华电技术, 2021, 43(5): 64-69.
[2]	刘义斌, 刘旋坤, 宋刚, 杨欣华, 张缦, 杨海瑞. 350 MW超临界煤粉锅炉全燃准东煤的运行优化研究[J]. 华电技术, 2021, 43(12): 79-84.
[3]	张俊伟. NG-M701F-R型余热锅炉高压过热器爆管原因分析及解决办法[J]. 华电技术, 2019, 41(7): 46-49.
[4]	王学礼. 1000MW超超临界锅炉过热器爆管原因分析及防范措施[J]. 华电技术, 2019, 41(7): 70-72.
[5]	王小军. 630MW超临界锅炉启动初期给水流量控制的探索[J]. 华电技术, 2019, 41(4): 74-75.
[6]	万立明，苏朋，周长文. 某600MW机组锅炉减温器混合管缺陷分析及优化改造[J]. 华电技术, 2019, 41(3): 53-55.
[7]	柯浩，李振梁，王曦. 超临界锅炉高温过热器爆管原因分析及对策[J]. 华电技术, 2019, 41(2): 26-27.
[8]	高清林1，郭开胜2. 330MW亚临界锅炉高温过热器爆管原因浅析[J]. 华电技术, 2018, 40(8): 26-27.
[9]	夏学敏. 600MW超超临界锅炉水冷壁爆管防治措施[J]. 华电技术, 2018, 40(8): 52-53.
[10]	陈永生. 锅炉末级过热器氧化皮堵塞爆管规律性偏差分析及处理[J]. 华电技术, 2018, 40(6): 23-25.
[11]	滕树会. 超超临界机组低温再热器失效分析[J]. 华电技术, 2018, 40(4): 36-39.
[12]	严晓哲1，杨平2. 电站锅炉氧化皮的防治研究[J]. 华电技术, 2018, 40(4): 42-44.
[13]	陈贤贤，房珏. 锅炉低温过热器爆管分析及预防措施[J]. 华电技术, 2018, 40(11): 55-56.
[14]	蔡泓铭. 660MW超超临界锅炉燃烧器改造及优化调整研究[J]. 华电技术, 2017, 39(6): 37-40.
[15]	李莉1，宋景慧2. 垃圾焚烧电厂过热器管腐蚀泄漏机制分析[J]. 华电技术, 2017, 39(4): 24-27.