汽轮机高压主汽门阀杆断裂原因分析及修复

华电技术 ›› 2015, Vol. 37 ›› Issue (5): 44-45.

汽轮机高压主汽门阀杆断裂原因分析及修复

江苏华电扬州发电有限公司, 江苏扬州 225002

出版日期:2015-05-25 发布日期:2015-10-08

Analysis on reason of fracture of valve stem of turbine HP main valve and repair

Jiangsu Huadian Yangzhou Power Generation Company Limited, Yangzhou 225002, China

Online:2015-05-25 Published:2015-10-08

摘要/Abstract

摘要：

摘要: 针对江苏华电扬州发电有限公司 #6 机组 #62 主汽门开关异常的情况, 通过分析确认主要故障发生在阀门机械部分, 解体蝶阀后发现阀杆从预启阀小弹簧室根部断裂｡分析了主汽门阀杆断裂的原因并提出了应对措施及检修方法｡

关键词: 关键词：汽轮机, 主汽门, 阀杆, 断裂, 修复

Abstract:

Abstract: Abnormal openclose phenomenon occurred in main steam valve No. 62 of unit No. 6 in Jiangsu Huadian Yangzhou Power Generation Company Limited.Aming at above problem,based on analysis, it was determined that the main failure occurred in mechanical part of the valve.The valve was disassembled, and it was found that the valve stem was fractured from the root segment in the small spring chamber of the preinlet valve.The reason of fracture of the valve stem of the main steam valve was analyzed, and the relevant countermeasures and repair method were proposed.

Key words:

font-family: E-HZ-PK74810c, color: black">Keywordsfont-family: SSJ-PK74820000002, color: black">:font-family: E-BZ-PK748e5, color: black">steam turbinefont-family: SSJ-PK74820000002, color: black">, font-family: E-BZ-PK748e5, color: black">main steam valvefont-family: SSJ-PK74820000002, color: black">, font-family: E-BZ-PK748e5, color: black">valve stemfont-family: SSJ-PK74820000002, color: black">, font-family: E-BZ-PK748e5, color: black">fracfont-family: E-BZ-PK748e5, color: black">turefont-family: SSJ-PK74820000002, color: black">, font-family: E-BZ-PK748e5, color: black">repair

徐敬民.

汽轮机高压主汽门阀杆断裂原因分析及修复[J]. 华电技术, 2015, 37(5): 44-45.

XU Jingmin.

Analysis on reason of fracture of valve stem of turbine HP main valve and repair[J]. Huadian Technology, 2015, 37(5): 44-45.

[1]	吴红辉1,王韦2. 20Cr1Mo1VNbTiB高温螺栓断裂失效分析[J]. 华电技术, 2018, 40(10): 27-29.
[2]	桑长勇，杜福明，高全海，李新建. BBD3854磨煤机螺旋输送器故障原因分析与对策[J]. 华电技术, 2017, 39(3): 57-59.
[3]	王曦. 17CrNiMo6磨煤机减速机齿轮轴断裂原因分析[J]. 华电技术, 2017, 39(10): 58-59.
[4]	雷清华1，王建文2，王政2. 风电塔筒P&H基础预应力高强锚杆断裂分析[J]. 华电技术, 2016, 38(8): 34-36.
[5]	贺杰. 燃料加热器天然气管道断裂故障分析及处理[J]. 华电技术, 2016, 38(6): 38-40.
[6]	彭钦春，赵显国. 汽轮发电机顶轴油分配器螺栓断裂故障分析及处理[J]. 华电技术, 2016, 38(6): 55-56.
[7]	李艳军，牛保献. 电厂排粉机电机大轴断裂原因分析[J]. 华电技术, 2016, 38(11): 38-39.
[8]	陈家权，刘福营，苏光耀，黄海鑫，吴根深. 超高压线夹端子断裂失效分析[J]. 华电技术, 2015, 37(4): 28-31.
[9]	贾少威. 空气压缩机轴颈断裂原因分析[J]. 华电技术, 2015, 37(11): 37-40.
[10]	杨小刚. 静叶可调轴流式引风机叶片磨损和断裂案例分析[J]. 华电技术, 2015, 37(10): 45-46.
[11]	冯玉锋. 斗轮堆取料机大轴断裂失效的原因分析[J]. 华电技术, 2014, 36(9): 37-39.
[12]	牛文献1，牛保献2. 某电厂循环水泵大轴断裂的原因分析[J]. 华电技术, 2014, 36(8): 27-29.
[13]	刘杰. 给水泵汽轮机高压汽源控制逻辑的改进[J]. 华电技术, 2014, 36(3): 32-33.
[14]	周凯. 直接空冷机组空冷岛轴流风机叶片断裂分析[J]. 华电技术, 2014, 36(2): 65-68.
[15]	侯健. 精密点检对高压电机转子笼条断裂的诊断应用分析[J]. 华电技术, 2013, 35(8): 52-53.