Cause analysis and the treatment on the boiler membrane wall leakage

Huadian Technology ›› 2009, Vol. 31 ›› Issue (5): 47-49.

• 技术交流 • Previous Articles Next Articles

Cause analysis and the treatment on the boiler membrane wall leakage

MI Hui

Yunfu Power Plant Corporation Limited, Guangdong Yudean Group Corporation Limited,Yunfu 527328, China

Received:1900-01-01 Revised:1900-01-01 Online:2009-05-25 Published:2009-05-25

Abstract

Abstract: This paper analyzes the membrane water wall leakage of the Yunfu Power Plant Corporation Limited of Guandong Yudean Groap corporation Limited No.4 boiler, it has been discovered that the stiffening bar unreasonable structure design was the primary reason to cause the problem occurring，by implementing the proposed basic method, the problem has been successfully solved，and the operation stability of the boiler membrane water wall has get a very great improvement.

Key words: membrane water wall leakage, stiffening bar, expand, crack, structure improvement, problem-solving method

MI Hui. Cause analysis and the treatment on the boiler membrane wall leakage[J]. Huadian Technology, 2009, 31(5): 47-49.

[1]	LI Penggang. Cause analysis for the leakage of serpentinetube elbow in supercritical boiler economizer [J]. Huadian Technology, 2020, 42(1): 68-72.
[2]	DENG Hui. Cause analysis on the fillet weld cracking of the outlet header socket of hightemperature reheater [J]. Huadian Technology, 2019, 41(8): 74-77.
[3]	HOU Jiaxu，ZHOU Shukang，LI Yanjun. Cause analysis of secondary blade cracking at the end of lowpressure rotor in a power plant [J]. Huadian Technology, 2019, 41(2): 28-31.
[4]	CHEN Li1，WU Chunchao2. Cause analysis and treatment of high moisture content of gypsum in 1050MW unit [J]. Huadian Technology, 2018, 40(5): 56-57.
[5]	CHEN Chunhui，YAO Zhiwei，DONG Yi. Causes and control methods of cracks on mortar pad for steam turbine in the cold and dry environment [J]. Huadian Technology, 2018, 40(2): 10-12.
[6]	CHEN Shenwei. Pump casing material and selection analysis of seawater cooling circulating pump [J]. Huadian Technology, 2018, 40(10): 40-42.
[7]	LIU Xinying1，LIU Jinqiu1，XIA Xiaotao1，LI Gen1，HAO Guangting2. Examples of treatments on welding cracks inside the thickwall 12Cr1MoV steel pipe [J]. Huadian Technology, 2018, 40(1): 55-56.
[8]	XU Zenghui1, ZHANG Chenliang2, WU Jicai2. Reason analysis and restoring treatments of face destruction for a certain concrete face rockfill dam [J]. Huadian Technology, 2017, 39(9): 45-47.
[9]	ZHOU Liping. BHW35 boiler longitudinal and circumferential weld defect analysis and control [J]. Huadian Technology, 2017, 39(8): 48-49.
[10]	SANG Changyong, DU Fuming, GAO Quanhai, LI Xinjian. Cause analysis and treatment of the fault of spiral conveyor in BBD3854 pulverizer [J]. Huadian Technology, 2017, 39(3): 57-59.
[11]	LUO Zhenxin1, DING Lianzheng2. SA738Gr.B steel welding cold crack sensitivity analysis [J]. Huadian Technology, 2017, 39(10): 44-45.
[12]	HUANG Chengbin. Cause analysis and treatments of face cracks for concrete face rockfill dam of Elesai Downstream Hydropower Station in Cambodia [J]. Huadian Technology, 2017, 39(10): 46-48.
[13]	GE Ting, GAO Kuan, LI Yong, LIANG Zhuo. 300MW bleeder turbine collision and friction cause analysis [J]. Huadian Technology, 2017, 39(1): 50-52.
[14]	ZHANG Jing1,ZHANG Zhongwen2,CHU Honghe1,LI Na1,SUN Chao1. GIS bellow expansion joint structure improvement [J]. Huadian Technology, 2016, 38(8): 8-11.
[15]	SHI Zedong, LIAO Yunbo. Analysis of 600MW unit platen superheater TP304H stainless steel elbow crack [J]. Huadian Technology, 2016, 38(3): 32-33.

Cause analysis and the treatment on the boiler membrane wall leakage

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments