Solution study of 1000MW boiler side water wall high temperature corrosion

Abstract

Abstract:

Abstract:After analyzing Huadian Laizhou Power Plant Company Limited No.2 boiler water wall high temperature corrosion causes,the plan of to provide side wind on the both side of furnace to reduce and prevent reducing atmosphere and high temperature corrosion on side water wall was claimed.After reconstruction,cheek damper opening test was carried out.Based the test result,the advantaged and notes of reconstruction plan were summarized.

Key words: Keywords:low , NO^_xburner, water wall, high temperature corrosion, reducing atmosphere, side wind, hot primary air, load

WEI Daojun. Solution study of 1000MW boiler side water wall high temperature corrosion[J]. Huadian Technology, 2016, 38(2): 1-5.

[1]	XIA Xuemin. Prevention measures for pipe bursting of water wall of 600MW ultrasupercritical boilers [J]. Huadian Technology, 2018, 40(8): 52-53.
[2]	LI Ge1, ZHU Haibao1, WANG Jun2. Reason analysis and prevention of the burnout of boiler burner nozzle [J]. Huadian Technology, 2018, 40(2): 21-24.
[3]	LI Guangwei,SUN Junwei,HUANG Qilong. 600MW opposed firing boiler water wall high temperature corrosion causes analysis and treatment [J]. Huadian Technology, 2016, 38(6): 43-46.
[4]	ZHANG Lei. Study and application of boiler water wall anti corrosion technology [J]. Huadian Technology, 2016, 38(5): 18-21.
[5]	SONG Kai, YUAN He, YOU Kunkun. Causes for corrosion and its treatment scheme of the heating surfaces in furnace of the 1000MW power plant [J]. Huadian Technology, 2016, 38(2): 9-10.
[6]	DONG Hongnian. Cause analysis and treatment of 1000MW ultra supercritical boiler water wall leakage [J]. Huadian Technology, 2016, 38(2): 48-52.
[7]	JIA Shaowei. Cause analysis of boiler water wall burst [J]. Huadian Technology, 2015, 37(12): 41-43.
[8]	YANG Feiping 1，YANG Zhu 1，TANG Zhenhua 2 . Solving scheme of water wall cracking for 600MW supercritical Wshaped flame boiler [J]. Huadian Technology, 2014, 36(1): 33-35.
[9]	WANG Tingguang. Treatment of defect of steel grit adhering on inner wall of tubes of boiler water wall [J]. Huadian Technology, 2013, 35(7): 38-39.
[10]	LIU Gang. Measures for preventing water wall overheating in wet/dry state transition process of ultra supercritical boiler [J]. Huadian Technology, 2013, 35(1): 4-6.
[11]	CHEN Kelu;RAO Hongjian. Analysis on reasons of hightemperature corrosion of water wall in 660MW unit boiler and countermeasures [J]. Huadian Technology, 2012, 34(5): 8-9.
[12]	WENG Jinyu. Analysis and prevention of tube crack of water wall in 600MW supercritical unit [J]. Huadian Technology, 2012, 34(2): 13-15.
[13]	ZHANG Zhenke;JI Guanghui;WANG Ying;YUAN Liqiang;LIU Wei. Analysis on reasons of jam fault of hot primary air valve in 600MW coalfired boiler and countermeasures [J]. Huadian Technology, 2012, 34(10): 34-36.
[14]	TANG Haoyi;SHENG Weimin. Analysis on cracks of water wall in 1 000 MW ultrasupercritical towertype oncethrough boiler and treatment [J]. Huadian Technology, 2011, 33(4): 44-46.
[15]	ZHENG Huixiana;XU Huifena;HE Libingb. Analysis on reasons of corrosion in inner wall of CFB boiler water wall tubes and treatment measures [J]. Huadian Technology, 2011, 33(4): 37-38.

Solution study of 1000MW boiler side water wall high temperature corrosion

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments