600MW opposed firing boiler water wall high temperature corrosion causes analysis and treatment

Huadian Technology ›› 2016, Vol. 38 ›› Issue (6): 43-46.

Previous Articles Next Articles

600MW opposed firing boiler water wall high temperature corrosion causes analysis and treatment

Guodian Science and Technology Research Institute，Nanjing 210031，China

Online:2016-06-25 Published:2016-09-21

Abstract

LI Guangwei,SUN Junwei,HUANG Qilong.

600MW opposed firing boiler water wall high temperature corrosion causes analysis and treatment

[J]. Huadian Technology, 2016, 38(6): 43-46.

[1]	XIA Xuemin. Prevention measures for pipe bursting of water wall of 600MW ultrasupercritical boilers [J]. Huadian Technology, 2018, 40(8): 52-53.
[2]	LI Ge1, ZHU Haibao1, WANG Jun2. Reason analysis and prevention of the burnout of boiler burner nozzle [J]. Huadian Technology, 2018, 40(2): 21-24.
[3]	ZHANG Lei. Study and application of boiler water wall anti corrosion technology [J]. Huadian Technology, 2016, 38(5): 18-21.
[4]	WEI Daojun. Solution study of 1000MW boiler side water wall high temperature corrosion [J]. Huadian Technology, 2016, 38(2): 1-5.
[5]	DONG Hongnian. Cause analysis and treatment of 1000MW ultra supercritical boiler water wall leakage [J]. Huadian Technology, 2016, 38(2): 48-52.
[6]	WANG Chengliang1,2. Failure analysis and its preventive measures for RUNBACK test of forced draft fans [J]. Huadian Technology, 2015, 37(8): 36-39.
[7]	JIA Shaowei. Cause analysis of boiler water wall burst [J]. Huadian Technology, 2015, 37(12): 41-43.
[8]	YANG Feiping 1，YANG Zhu 1，TANG Zhenhua 2 . Solving scheme of water wall cracking for 600MW supercritical Wshaped flame boiler [J]. Huadian Technology, 2014, 36(1): 33-35.
[9]	WANG Tingguang. Treatment of defect of steel grit adhering on inner wall of tubes of boiler water wall [J]. Huadian Technology, 2013, 35(7): 38-39.
[10]	LIU Gang. Measures for preventing water wall overheating in wet/dry state transition process of ultra supercritical boiler [J]. Huadian Technology, 2013, 35(1): 4-6.
[11]	CHEN Kelu;RAO Hongjian. Analysis on reasons of hightemperature corrosion of water wall in 660MW unit boiler and countermeasures [J]. Huadian Technology, 2012, 34(5): 8-9.
[12]	WENG Jinyu. Analysis and prevention of tube crack of water wall in 600MW supercritical unit [J]. Huadian Technology, 2012, 34(2): 13-15.
[13]	ZHENG Huixiana;XU Huifena;HE Libingb. Analysis on reasons of corrosion in inner wall of CFB boiler water wall tubes and treatment measures [J]. Huadian Technology, 2011, 33(4): 37-38.
[14]	TANG Haoyi;SHENG Weimin. Analysis on cracks of water wall in 1 000 MW ultrasupercritical towertype oncethrough boiler and treatment [J]. Huadian Technology, 2011, 33(4): 44-46.
[15]	CHEN Jianjun. Analysis on leakage reasons of the tubes in water wall of a power plant boiler No.2 [J]. Huadian Technology, 2011, 33(1): 53-54.

600MW opposed firing boiler water wall high temperature corrosion causes analysis and treatment

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments