Reasons analysis on of T92 steel pipe bursting of high temperature superheater

Huadian Technology ›› 2011, Vol. 33 ›› Issue (3): 24-28.

• 研究与开发 • Previous Articles Next Articles

Reasons analysis on of T92 steel pipe bursting of high temperature superheater

DONG Hongnian

Guangdong Datang International Chaozhou Power Generation Corporation Limited, Chaozhou 515723, China

Received:1900-01-01 Revised:1900-01-01 Online:2011-03-25 Published:2011-03-25

Abstract

Abstract: The T92 steel outlet pipe of high temperature superheater of a power plant bursted. The normal temperature tensile test and the high temperature tensile test for the cracked pipe and six pipes around the cracked pipe were carried out respectively. Combining with the practical site situation and through comparison and analysis of test results, the real reasons of this pipe crack accident were investigated, and relevant measures were proposed for preventing the pipe crack occurring once again.

Key words: T92 steel, pipe bursting, reason analysis, tensile test, high-temperature strength, metallographic structure, overheat failure

DONG Hongnian. Reasons analysis on of T92 steel pipe bursting of high temperature superheater[J]. Huadian Technology, 2011, 33(3): 24-28.

[1]	LI Ge，ZHU Haibao，QIAO Lijie，CHEN Zhuoting. Quality evaluation and performance analysis of WC9 cast steel safety valve for inservice units in a thermal power plant [J]. Huadian Technology, 2019, 41(9): 72-75.
[2]	XIA Xuemin. Prevention measures for pipe bursting of water wall of 600MW ultrasupercritical boilers [J]. Huadian Technology, 2018, 40(8): 52-53.
[3]	LI Ge1, ZHU Haibao1, WANG Jun2. Reason analysis and prevention of the burnout of boiler burner nozzle [J]. Huadian Technology, 2018, 40(2): 21-24.
[4]	ZHANG Xuehai. On line replacement of valve servo valve and the analysis of the servo valve jam of 600MW steam turbine [J]. Huadian Technology, 2016, 38(2): 35-38.
[5]	PENG Jun. Analysis and processing on fault reason of pneumatic brake system of hydropower unit No.1 in Huanglongtan Hydropower Plant [J]. Huadian Technology, 2015, 37(2): 42-43.
[6]	ZHENG Jianfeng. Analysis on reasons of higher temperature of bearing bush of horizontal shaft mixed flow water turbinegenerator unit and treatment scheme [J]. Huadian Technology, 2015, 37(1): 34-36.
[7]	FENG Yufeng. Analysis on reasons of fracture failure of main shaft of bucketwheel stackerreclaimer [J]. Huadian Technology, 2014, 36(9): 37-39.
[8]	LI Qiufeng, LIU Shuwei. Function perfecting of distributed control system of 600MW unit [J]. Huadian Technology, 2014, 36(8): 14-16.
[9]	WU Fan. Analysis on reasons caused tripping of generator reverse power protection of S109FA combined cycle unit [J]. Huadian Technology, 2014, 36(4): 57-60.
[10]	HAN Lizheng. Analysis on reasons of outoflimit vibration of water intake pump [J]. Huadian Technology, 2014, 36(11): 55-57.
[11]	YANG Feiping 1，YANG Zhu 1，TANG Zhenhua 2 . Solving scheme of water wall cracking for 600MW supercritical Wshaped flame boiler [J]. Huadian Technology, 2014, 36(1): 33-35.
[12]	XU Gang. Analysis on reason of damage of clamping bolt passing through core of generator stator and treatment method [J]. Huadian Technology, 2014, 36(1): 58-59.
[13]	JIANG Anwei. Analysis on reasons of maloperation of 500kV line sweitch and precontrol measures [J]. Huadian Technology, 2014, 36(1): 63-65.
[14]	HAN Xianghu. Analysis on reasons of switch tripping caused by interrupt of 110V DC power source [J]. Huadian Technology, 2013, 35(9): 1-3.
[15]	BU Fanwei, NI Jianmin. Analysis on reasons of fault of compensation capacitor in 6kV ungrounded system [J]. Huadian Technology, 2013, 35(9): 7-8.

Reasons analysis on of T92 steel pipe bursting of high temperature superheater

Knowledge

Cited

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments